0Cr25Al5
Chemical Content(%)
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max0.06 | Max 0.025 | Max 0.025 | Max 0.70 | Max 1.0 | 23.0~26.0 | Max 0.60 | 4.5~6.5 | Bal. | - |
Mechanical Properties
| Max Continuous Service Temp | 1250ºC |
| Resisivity at 20ºC | 1.42±0.06 ohm mm2/m |
| Density | 7.10 g/cm3 |
| Thermal Conductivity | 46.1KJ/m·h·ºC |
| Coefficient of Thermal Expansion | 16.0×10-6/ºC |
| Melting Point | 1500ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
Furnace resistance alloy heating wire
1. A quite reasonable price
2. Stable performance:
3 high working temperature
Furnace resistance alloy heating wire
Specification:
We specializing in Ferro-Chrome (Fe-Cr-AL) wire, Nickel-Chrome (Nichrome) wire, Copper Nickel (Constantan) wire, Stainless steel wire and related products in alloys tailored to meet specific customer requirements.
Round wire from SWG 0 to SWG 48(Dia 0.04mm-8.0mm).
Ribbon/strip: Thickness: 0.04mm-0.75mm
Width: 0.08mm-6.0mm
Our furnace resistance alloy heating ribbon is of high quality with following features:
1. A quite reasonable price
2. Stable performance: High working temperature(The highest temperature can be 1400), high strength under temperature, corrosion resistance, long life-span, allowable high surface load, small specific gravity, good formability and weldability.
Delivery status and supply state of furnace resistance alloy heating ribbon
Wire and plate with the looseness or oxidation colour soft modal supply.
Strip except special requirements outside, general with after annealing oxidation colour supply.
The flat silk thread and protecting gas to light after annealing soft modal supply.
2, product packaging of furnace resistance alloy heating ribbon
Wire or strips to pack cloth bandaged volumes supply.
Thread and flat silk, axis encapsulate supply.
1, when the design should be based on the power wiring method, reasonable surface load, the correct choice of silk diameter,
2, before installation coping furnace thorough examination, cleared ferritic, "carbon, and the electric stove contact risks to avoid short circuit, in case caused furnace silk breakdown,
3, when installation should press design wiring method properly connected;
4, in use before should check the sensitivity of the temperature control system, in case of failure, cause temperature burnt.
Product Tags:
|
|
Cold Rolled Fecral Electric Resistance Wire Good Oxidation Resistance Images
|